機械用碳石墨材料類別/型號及技術性能
作者：http://www.www.siemnes68.com
發布時間：2019-09-14 01:15:13
機械用碳石墨材料類別/型號及技術性能
機械用碳石墨材料類別/型號及技術性能 |
| 型號 Type | 浸漬材料 Impregnated Material | 體積密度 BulkDensity g/cm3 (≥) | 抗折強度 Transverse Strength Mpa(≥) | 抗壓強度 Conpressive Strength Mpa (≥) | 肖氏硬度 Hardness Shore (≥) | 氣孔率% Porosity (≤) | 熱膨脹系數 Coeffcient of Expansion X10-6 /℃ | 使用溫度℃ Nax.Suitable Temperature |
| 碳石墨 Pure Carbon Graphite | ||||||||
| XH-M191 | 純碳石墨 | 1.75 | 85 | 150 | 90 | 1.2 | 600 | |
| XH-M126 | 碳石墨（T) | 1.60 | 40 | 100 | 65 | 12.0 | 400 | |
| XH-M254 | 1.70 | 25 | 45 | 40 | 20.0 | 450 | ||
| XH-M238 | 1.70 | 35 | 75 | 40 | 15.0 | 450 | ||
| 浸漬樹脂石墨 Resin-Impregnated Graphite | ||||||||
| XH-M106H | 環氧樹脂 Epoxy Resin (H) | 1.75 | 65 | 200 | 85 | 1.5 | 210 | |
| XH-M120H | 1.70 | 60 | 200 | 85 | 1.5 | |||
| XH-M126H | 1.70 | 55 | 160 | 80 | 1.5 | |||
| XH-M180H | 1.80 | 80 | 220 | 90 | 1.5 | |||
| XH-M254H | 1.80 | 35 | 75 | 42 | 1.5 | |||
| XH-M238H | 1.88 | 50 | 105 | 55 | 1.5 | |||
| XH-M106K | 呋喃樹脂 Furan Resin (k) | 1.75 | 65 | 200 | 90 | 1.5 | 210 | |
| XH-M120K | 1.70 | 60 | 200 | 85 | 1.5 | |||
| XH-M126K | 1.70 | 60 | 170 | 85 | 1.5 | |||
| XH-M180K | 1.80 | 80 | 220 | 90 | 1.5 | |||
| XH-M238K | 1.85 | 55 | 105 | 55 | 1.5 | |||
| XH-M254K | 1.80 | 40 | 80 | 45 | 1.5 | |||
| XH-M180F | 酚醛樹脂 Phenolic Resin (F) | 1.80 | 70 | 220 | 90 | 1.5 | 210 | |
| XH-M106F | 1.75 | 60 | 200 | 85 | 1.5 | |||
| XH-M120F | 1.70 | 55 | 190 | 80 | 1.0 | |||
| XH-M126F | 1.70 | 50 | 150 | 75 | 1.5 | |||
| XH-M238F | 1.88 | 50 | 105 | 55 | 1.5 | |||
| XH-M254F | 1.80 | 35 | 75 | 45 | 1.0 | |||
| 浸漬金屬石墨 Metal-Impregnated Graphite | ||||||||
| XH-M120B | 巴氏合金 Babbitt (B) | 2.40 | 60 | 160 | 65 | 9.0 | 210 | |
| XH-M254B | 2.40 | 40 | 70 | 40 | 8.0 | |||
| XH-M106D | 銻 Antimony (D) | 2.20 | 75 | 190 | 70 | 2.5 | 400 | |
| XH-M120D | 2.20 | 70 | 180 | 65 | 2.5 | |||
| XH-M254D | 2.20 | 40 | 85 | 40 | 2.5 | 450 | ||
| XH-M106P | 銅合金 Copper Alloy (P) | 2.60 | 70 | 240 | 70 | 3.0 | 400 | |
| XH-M120P | 2.40 | 75 | 250 | 75 | 3.0 | |||
| XH-M254P | 2.60 | 40 | 120 | 45 | 3.0 | 450 | ||
| 樹脂粘合石墨 Resin Graphite | ||||||||
| XH-301 | 熱壓石墨 | 1.70 | 50 | 98 | 62 | 1.0 | 200 | |
| XH-302 | 熱壓石墨 | 1.65 | 55 | 105 | 58 | 1.0 | 180 | |
機械用碳石墨材料的耐化學腐蝕性能
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
注：“+”為穩定；“-”為不穩定； “O”為較穩定 。 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||